              Plastic granulator production How to prevent plastic discoloration (Ke Rui Te)
              Update time: 2017-08-31 Click: 1528 times
               Plastic granulator production How to prevent plastic discoloration (Ke Rui Te):
              Material discoloration is usually due to charred or degraded and other reasons.
              ① material problems
              A. Material contamination;
              B. Material is not dry;
              C. Too much volatiles in the material;
              D. Material degradation;
              E. Colorant decomposition;
              F. Additive decomposition.
              ② Extrusion equipment problems
              A. Equipment is not clean;
              B. Dry matter is not clean;
              C. Ambient air is not clean, coloring agent floating in the air, deposited in the hopper and his parts;
              D. Thermocouple failure;
              E. Temperature control system failure;
              F. Resistance electric heating (or far infrared heating device) damage;
              G. There is an obstruction in the cartridge to cause the material to degrade.
              ③ temperature problems
              A. Cylinder temperature is too high, lower cylinder temperature;
              B. The nozzle temperature is too high to reduce the nozzle temperature.
              ④ out of the problem
              A. Reduce the screw speed;
              B. Reduce the back pressure;
              C. Reduce the clamping force;
              D. Reduce the extrusion pressure;
              E. Shorten the extrusion pressure;
              F. Shorten the full pressure time;
              G. Slow down the extrusion speed;
              H. Shorten the extrusion cycle.
              ⑤ Extrusion die problem
              Consider the mold exhaust;
              B. Increase the gate size, reduce the shear rate;
              C. Increase the nozzle hole, the main channel and the size of the diversion channel;
              D. Removal of in-mold oils and lubricants;
              Adjust the oiling agent.
              In addition, high impact strength of polystyrene and ABS, such as products, stress, but also due to stress and discoloration. Kellett